Lẹhin ti ṣayẹwo ati idanwo ohun elo ọpa irin alloy yika, iṣelọpọ le bẹrẹ ni ibamu si iwọn ti bọọlu irin.Awọn irin forging ti wa ni kikan si kan awọn iwọn otutu nipa intermediating pẹlu igbohunsafẹfẹ ileru lati rii daju awọn munadoko iran ti oniyipada ninu awọn forging;Awọn ayederu irin pupa-gbona ti wa ni fifiranṣẹ sinu afẹfẹ afẹfẹ ati ṣiṣe nipasẹ awọn oniṣẹ oye.Lẹhin ti ṣe agbekalẹ bọọlu irin gbigbona pupa lẹsẹkẹsẹ sinu JUNDA ti a ṣe apẹrẹ awọn ohun elo itọju ooru ni pataki fun piparẹ ati itọju igbona, iye líle giga ati aṣọ ti bọọlu irin le rii daju.
1.High ikolu toughness
2.Compact agbari
3.High yiya resistance
4.Low breakage oṣuwọn
5.Uniform líle
6.Ko si abuku
Apo apoti | Irin Ilu | |
Apapọ iwuwo 1000kgs fun gbogbo awọn boolu iwọn | Iwọn boolu | Apapọ iwuwo |
20-30mm | 930-1000KGS | |
40-60mm | 900-930KGS | |
70-90mm | 830-880KGS | |
100mm ati loke | 830-850KGS | |
Apo:73× 60cm, 1.5KG, 0.252CBMÌlù:60×90cm, 15-20KG, 0.25CBM Pallet Nikan: 60× 60× 9cm, 4-6KG:Ilọpo meji:120×60×10cm, 12-14KG |
Imọ paramita ti forging irin rogodo | ||||||||||||
Inṣi | Iwọn | T iwuwo | Ifarada (mm) | Ohun elo | Lile oju (HRC) | Lile iwọn didun (HRC) | ||||||
3/4" | D20mm | 0.037+/-0.005 | 2+/-1 | B2 | 63-66 | 63-66 | ||||||
1" | D25mm | 0.072+/-0.01 | 2+/-1 | B2 | 63-66 | 63-66 | ||||||
11/4" | D30mm | 0.13+/-0.02 | 2+/-1 | B2 | 63-66 | 63-66 | ||||||
11/2" | D40mm | 0.30+/-0.04 | 2+/-1 | B2 | 62-66 | 62-66 | ||||||
2" | D50mm | 0.6+/-0.05 | 2+/-1 | B2 | 62-65 | 61-64 | ||||||
21/2" | D60mm | 1.0+/-0.05 | 2+/-1.5 | B2 | 62-65 | 60-62 | ||||||
3" (yiyi gbona) | D80mm | 2.0+/-0.06 | 3+/-2 | B3 | 60-63 | 60-62 | ||||||
3"(Eda) | D80mm | 2.1+/-0.06 | 3+/-2 | B3 | 60-62 | 53-57 | ||||||
31/2" | D90mm | 3.0+/-0.07 | 3+/-2 | B3 | 60-63 | 59-62 | ||||||
4" | D100mm | 4.1+/-0.15 | 3+/-2 | B3 | 60-63 | 59-62 | ||||||
5" | D125mm | 8.1+/-0.3 | 3+/-2 | B3 | 59-62 | 55-60 | ||||||
Kemikali tiwqn | C% | Si% | Mn% | Kr% | P% | S% | Ni% | |||||
B2 | 0.72-1.03 | 0.15-0.35 | 0.3-1.2 | 0.2-0.6 | ≤0.035 | ≤0.035 | i≤0.25 | |||||
B3 | 0.53-0.88 | 1.2-2.00 | 0.50-1.20 | 0.7-1.20 | ≤0.035 | ≤0.035 | i≤0.25 |